| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Eccentric load | 偏心载荷 |
The external load on a fastener or groups of fasteners is said to be eccentric if the resultant of that load does not pass through the centroid of the group of fasteners (eccentric shear load ) or does not coincide with the bolt axis (eccentric tensile load ). 如果一个或多个紧固件上的外部载荷的合力未穿过紧固件组的质心（偏心剪切载荷）或与螺栓轴不重合（偏心拉伸载荷），则称该外部载荷为偏心。 |
| Edge distance | 边距 |
The distance from the edge of a bearing specimen to the center of the hole in the direction of applied force. 在作用力方向上，从轴承试样的边缘到孔中心的距离。 |
| Edge distance ratio | 边距比 |
The ratio of the edge distance to the pin diameter in a bearing test. 轴承测试中边缘距离与销直径的比值。 |
| Effective crack size (ae) | 有效裂纹尺寸（ae） |
The physical crack size augmented for the effects of cracking plastic deformation. Sometimes the effective crack size is calculated from a measured value of a physical crack size plus a calculated value of a plastic-zone adjustment. A preferred method for calculation of effective crack size compares compliance from the secant of a load-deflection trace with the elastic compliance from a calibration for the type of specimen. 由于裂纹塑性变形的影响，物理裂纹尺寸增大。有时，根据物理裂纹尺寸的测量值加上塑性区调整的计算值来计算有效裂纹尺寸。计算有效裂纹尺寸的首选方法是将载荷-挠度轨迹正割的柔度与试样类型校准的弹性柔度进行比较。 |
| Effective discharge area (Unit m²) | 有效排放面积（单位m²） |
A nominal area for flow through a pressure relief valve used to determine the valve’s flow capacity given the pressure difference across it, the fluid density and correction factors to allow for compressibility, the back pressure and the coefficient of discharge. 流经泄压阀的标称面积，用于确定阀门的流量，给定压力差、流体密度和允许可压缩性的校正因子、背压和排放系数。 |
| Effective length of a bolt | 螺栓的有效长度 |
The grip length plus some portion of the bolt (often one-half of the thickness of the nuts) which lies within the nut(s) plus some portion (often one-half the thickness) of the head. 握持长度加上位于螺母内的螺栓的某些部分（通常是螺母厚度的二分之一）加上头部的某些部分（通常是厚度的二分之一）。 |
| Effective radius of nut, bolt head, or threads | 螺母、螺栓头或螺纹的有效半径 |
Distance between the geometric center of the part and the circle of points through which the resultant contact forces between mating parts passes. Must be determined by integration. 零件几何中心与配合零件之间的合力通过的点圆之间的距离。必须通过积分来确定。 |
| Effective yield strength | 有效屈服强度 |
An assumed value of uniaxial yield strength that represents the influence of plastic yielding on fracture test parameters. 单轴屈服强度的假设值，代表塑性屈服对断裂试验参数的影响。 |
| Elastic calibration device | 弹性校准装置 |
A device for use in verifying the load readings of a testing machine consisting of an elastic member(s) to which loads may be applied, combined with a mechanism or device for indicating the magnitude (or a quantity proportional to the magnitude) of deformation under load. 一种用于验证试验机载荷读数的装置，由可施加载荷的弹性构件组成，与指示载荷下变形量（或与该量成比例的量）的机构或装置相结合。 |
| Elastic constants | 弹性常数 |
The factors of proportionality that relate elastic displacement of a material to applied forces. 将材料的弹性位移与施加的力相关联的比例因子。 |
| Elastic deformation | 弹性变形 |
A change in dimensions directly proportional to and in phase with an increase or decrease in applied force. 尺寸的变化与施加的力的增加或减少成正比并同相。 |
| Elastic energy | 弹性能 |
The amount of energy required to deform a material within its elastic range of behavior, neglecting small heat losses due to internal friction. The energy absorbed by a specimen per unit volume of material contained within the gage length being tested. It is determined by measuring the area under the stress-strain curve up to a specified elastic strain. See also modulus of resilience and strain energy. 材料在其弹性行为范围内变形所需的能量，忽略因内耗引起的小热损失。试样在被测标距内每单位体积材料吸收的能量。它是通过测量应力-应变曲线下达到规定弹性应变的面积来确定的。另见弹性模量和应变能。 |
| Elastic interactions | 弹性相互作用 |
When a bolt is tightened it partially compresses the joint members ‘‘in its own neighborhood.’’ When nearby bolts are tightened later, they further compress the joint in this region. This allows the first bolt to relax a little (lose a little preload). Tightening bolts on the opposite side of the joint, however, might increase preload in some of the earlier bolts tightened on the near side. These shifts and changes in the elastic energy stored in individual bolts, during assembly, are called elastic interactions. 当螺栓拧紧时，它会“在其自身附近”部分压缩接头构件稍后拧紧附近的螺栓时，进一步压缩该区域的接头。这允许第一个螺栓稍微松弛（失去一点预载）。但拧紧接头另一侧的螺栓可能会增加早期在近侧拧紧的一些螺栓的预载。在装配过程中，储存在单个螺栓中的弹性能量的这些位移和变化称为弹性相互作用。 |
| Elastic limit | 弹性极限 |
The maximum stress which a material is capable of sustaining without any permanent strain (deformation) remaining on complete release of the stress. 材料在完全释放应力时能够承受的最大应力，且不会留下任何永久应变（变形）。 |
| Elastic recovery | 弹性恢复 |
Amount the dimension of a stressed elastic material returns to its original (unstressed) dimension on release of an applied load. In hardness testing, the shortening of the original dimensions of the indentation upon release of the applied load. 在释放施加的载荷时，受应力弹性材料的尺寸恢复到其原始（无应力）尺寸的量。在硬度测试中，当释放所施加的载荷时，压痕的原始尺寸缩短。 |
| Elastic resilience | 弹性回弹 |
The amount of energy absorbed in stressing a material up to the elastic limit; or, the amount of energy that can be recovered when stress is released from the elastic limit. 向材料施加应力直至弹性极限所吸收的能量；或者当应力从弹性极限释放时可以恢复的能量值。 |
| Elastic strain energy | 弹性应变能 |
The energy expended by the action of external forces in deforming a body elastically. Essentially, all the work performed during elastic deformation is stored as elastic energy, and this energy is recovered upon release of the applied force. 在外力作用下使物体弹性变形所消耗的能量。本质上，弹性变形过程中所做的所有功都以弹性能的形式存储，并且在释放所施加的力时恢复该能量。 |
| Elasticity | 弹性 |
The property of a material by virtue of which deformation caused by stress disappears on removal of the stress. A perfectly elastic body completely recovers its original shape and dimensions after release of stress. 一种材料的特性，通过这种特性，由应力引起的变形在去除应力后消失。完全弹性体在应力释放后完全恢复其原始形状和尺寸。 |
| Elbow | 肘部 |
1. A fitting that connects the ends of two pipes at an angle, 45°, 90°, and 180° being the most common. 2. The third joint on an articulated robot corresponding to the human elbow. 1.以45°、90°和180°角连接两个管道端部的配件。2.示例关节机器人上的第三关节对应于人的肘部。 |
| Electrode | 电极 |
The two metallic bodies in a battery or Corrosion cell which give up electrons (the Anode) or which attract them (the Cathode). 电池或腐蚀电池中释放电子（阳极）或吸引电子（阴极）的两个金属体。 |
| Electrolyte | 电解质 |
The liquid with which the Electrodes of a battery or Corrosion cell are wetted. 润湿电池或腐蚀电池电极的液体。 |
| Electroplating | 电镀 |
Deposition of one metal on to another using electrolysis. The metal to be plated forms the cathode in an electrolytic cell, and the metal to be deposited forms the anode. 使用电解将一种金属沉积到另一种金属上。待镀金属形成电解池中的阴极，待沉积金属形成阳极。 |
| Elongation | 伸张率 |
A term used in mechanical testing to describe the amount of extension of a test piece when stressed. 机械测试中使用的术语，用于描述试样在受力时的延伸量。 |
| Elongation measurement | 伸张率测量 |
Bolt elongation is directly proportional to axial stress when the applied stress is within the elastic range of the material. If both ends of a bolt are accessible, a micrometer measurement of bolt length made before and after the application of tension will ensure the required axial stress is applied. 当施加的应力在材料的弹性范围内时，螺栓伸长率与轴向应力成正比。如果螺栓的两端都可以接近，则在施加张力前后对螺栓长度进行测微计测量，以确保施加所需的轴向应力。 |
| Embedment | 嵌入 |
Localized plastic deformation in heavily loaded fasteners allows one part to sink into, or smooth the surface of, a softer or more heavily loaded second part. Nuts embed themselves in joint surfaces. Bolt threads embed themselves in nut threads, etc. 重载紧固件中的局部塑性变形允许一个零件陷入较软或更重载的第二零件中，或使其表面光滑。螺母嵌入接合面中。例如螺栓螺纹嵌入螺母螺纹等。 |
| Embrittlement | 脆化 |
The loss of ductility or fracture toughness of materials, either during processing or in service. The severe loss of ductility or toughness or both, of a material, usually a metal or alloy. Many forms of embrittlement can lead to brittle fracture. Many forms can occur during thermal treatment or elevated-temperature service (thermally induced embrittlement). Some of these forms of embrittlement, which affect steels, include blue brittleness, 885 °F (475 °C) embrittlement, quench-age embrittlement, sigma-phase embrittlement, strain-age embrittlement, temper embrittlement, tempered martensite embrittlement, and thermal embrittlement. In addition, steels and other metals and alloys can be embrittled by environmental conditions (environmentally assisted embrittlement). The forms of environmental embrittlement include acid embrittlement, caustic embrittlement, corrosion embrittlement, creep-rupture embrittlement, hydrogen embrittlement, liquid metal embrittlement, neutron embrittlement, solder embrittlement, solid metal embrittlement, and stress-corrosion cracking. 材料在加工或使用过程中的延展性或断裂韧性损失。通常是金属或合金的延展性或韧性或两者的严重损失。多种形式的脆化可导致脆性断裂。在热处理或高温服务期间，可能会出现多种形式（热致脆化）。影响钢的一些脆化形式包括蓝脆、885°F（475°C）脆化、淬火时效脆化、西格玛相脆化、应变时效脆化，回火脆化、回火马氏体脆化和热脆化。此外，钢和其他金属和合金可能因环境条件而脆化（环境辅助脆化）。环境脆化的形式包括酸脆化、碱脆化、腐蚀脆化、蠕变断裂脆化、氢脆化、液态金属脆化、中子脆化、焊料脆化、固态金属脆化和应力腐蚀开裂。 |
| End-quench hardenability test | 端淬淬透性试验 |
A laboratory procedure for determining the hardenability of a steel or other ferrous alloy. Hardenability is determined by heating a standard specimen above the upper critical temperature, placing the hot specimen in a fixture so that a stream of cold water impinges on one end, and, after cooling to room temperature is completed, measuring the hardness near the surface of the specimen at regularly spaced intervals along its length. The data are normally plotted as hardness versus distance from the quenched end. 测定钢或其他铁合金淬透性的实验室程序。淬透性是通过将标准试样加热到高于上临界温度，将热试样放置在夹具中，使冷水流冲击一端，并在冷却至室温后，沿试样长度以规则间隔测量试样表面附近的硬度来确定的。数据通常绘制为硬度与距淬火端距离的关系。 |
| Endurance | 耐力 |
The capacity of a material to withstand repeated application of stress. 材料承受反复施加应力的能力。 |
| Endurance limit | 耐力极限 |
The maximum stress below which a material can presumably endure an infinite number of stress cycles. The value of the maximum stress and the stress ratio also should be stated. That completely reversing stress limit below which a bolt or joint member will have an essentially infinite life under cyclic fatigue loads. Note that the mean stress on the bolts here is zero. 材料可以承受无限次应力循环的最大应力。还应说明最大应力值和应力比。完全逆转的应力极限，低于该极限螺栓或接头构件在循环疲劳载荷下将具有基本上无限的寿命。请注意，此处螺栓上的平均应力为零。 |
| Energy losses (Unit kJ) | 能量损失（单位kJ） |
A commonly-used misnomer in view of the conservation-ofenergy principle, but used to mean energy converted into forms that are not used in a process, for example thermal energy from a heat engine dissipated to the surroundings, or produced by friction in a machine, or by surface drag. 从能量守恒原理来看，这是一个常用的术语错误，但可以用于表示转换为过程中未使用的形式的能量，例如，从热机散发到周围环境的热能，或由机器中的摩擦或表面阻力产生的热能。 |
| Engine | 引擎 |
A machine that converts energy, including the chemical energy in a fuel and electrical energy, into mechanical energy, usually to produce power delivered through a rotating shaft or thrust. Examples include internal-combustion engines, gas and steam turbines, rocket engines, electric, hydraulic and pneumatic motors. 一种将能量（包括燃料中的化学能和电能）转换为机械能的机器，通常通过旋转轴或推力产生动力。例子包括内燃机、燃气轮机和蒸汽轮机、火箭发动机、电动、液压和气动马达。 |
| Engine emissions | 发动机排放 |
(exhaust emissions) The pollutants contained in the exhaust gases from an internal-combustion engine. （废气排放）内燃机废气中所含的污染物。 |
| Engineering strain (e) | 工程应变（e） |
A term sometimes used for average linear strain or conventional strain in order to differentiate it from true strain. In tension testing it is calculated by dividing the change in the gage length by the original gage length. 一个术语，有时用于平均线性应变或常规应变，以便将其与真实应变区分开来。在张力测试中，通过将标距变化除以原始标距来计算。 |
| Engineering stress (s) | 工程应力 |
A term sometimes used for conventional stress in order to differentiate it from true stress. In tension testing, it is calculated by dividing the breaking load applied to the specimen by the original crosssectional area of the specimen. 一个术语，有时用于常规应力，以区别于真实应力。在拉伸试验中，通过将施加在试样上的断裂载荷除以试样的原始横截面积来计算。 |
| Equation, long form | 方程，长格式 |
An equation which relates the torque applied to a bolt to the preload created in it, and involves fastener geometry and the coefficient of friction between mating surfaces. A theoretical equation based on rigid body mechanics and the assumption that the geometry of the fastener is perfectly described by blueprint dimensions. 将施加在螺栓上的扭矩与螺栓中产生的预载荷联系起来的方程，该方程涉及紧固件几何形状和配合面之间的摩擦系数。基于刚体力学和紧固件几何结构由蓝图尺寸完美描述的假设的理论方程。 |
| Equation, short form | 方程式，简写形式 |
An empirical equation which relates the torque applied to the bolt to the preload created in it, and which depends mainly on an experimentally derived factor called the Nut factor. 一个经验公式，将施加在螺栓上的扭矩与螺栓中产生的预载荷联系起来，主要取决于一个称为螺母系数的实验得出的系数。 |
| Equilibrium diagram | 平衡图 |
A graphical representation of the temperature, pressure and composition limits of phase fields in an alloy system as they exist under conditions of complete equilibrium. In metal systems, pressure is usually considered constant. 在完全平衡条件下，合金系统中相场的温度、压力和成分极限的图形表示。在金属系统中，压力通常被认为是恒定的。 |
| Erosion | 侵蚀 |
Progressive loss of original material from a solid surface due to mechanical interaction between that surface and a fluid, a multicomponent fluid, or impinging liquid or solid particles. 由于固体表面与流体、多组分流体或撞击液体或固体颗粒之间的机械相互作用，原始材料从固体表面逐渐损失。 |
| Essential conditions | 必要条件 |
Each type of failure to which bolted joints are subject is set up by three or four conditions. The conditions vary, depending on the mode of failure, but never number more than four. Eliminating any one of the essential conditions for a particular type of failure can prevent that type of failure. 螺栓连接所遭受的每种类型的故障都由三个或四个条件确定。根据故障模式的不同，情况会有所不同，但数量不得超过四个。消除特定类型故障的任何一个基本条件都可以防止该类型故障。 |
| Eutectic | 共晶 |
(1) An isothermal reversible reaction in which a liquid solution is converted into two or more intimately mixed solids on cooling, the number of solids formed being the same as the number of components in the system. (2) An alloy having the composition indicated by the eutectic point on an equilibrium diagram. (3) An alloy structure of intermixed solid constituents formed by a eutectic reaction. （1）一种等温可逆反应，其中液体溶液在冷却时转化为两种或两种以上紧密混合的固体，形成的固体数量与系统中组分的数量相同。（2）一种合金，其成分由平衡图上的共晶点表示。（3）由共晶反应形成的混合固体成分的合金结构。 |
| Eutectic carbide | 共晶碳化物 |
Carbide formed during freezing as one of the mutually insoluble phases participating in the eutectic reaction of ferrous alloys. 在冷冻过程中形成的碳化物，是参与铁合金共晶反应的互不溶相之一。 |
| Eutectic melting | 共晶熔化 |
Melting of localized microscopic areas whose composition corresponds to that of the eutectic in the system. 局部微观区域的熔化，其成分对应于系统中的共晶成分。 |
| Eutectoid | 共析 |
(1) An isothermal reversible reaction in which a solid solution is converted into two or more intimately mixed solids on cooling, the number of solids formed being the same as the number of components in the system. (2) An alloy having the composition indicated by the eutectoid point on an equilibrium diagram. (3) An alloy structure of intermixed solid constituents formed by a eutectoid reaction. （1）一种等温可逆反应，其中固溶体在冷却时转化为两种或两种以上紧密混合的固体，形成的固体数量与系统中组分的数量相同。（2）具有平衡图上共析点所示成分的合金。（3）由共析反应形成的混合固体成分的合金结构。 |
| Expansion bolt | 膨胀螺栓 |
When a through bolt cannot be used for attaching a pipe hanger, bracket, or other part, to a wall or ceiling of brick or concrete, what are known as expansion bolts are often used. The body of an expansion bolt is divided and the arrangement is such that, when the head of the bolt is turned, the sections forming the body of the bolt are forced outward and against the wall of the hole which has been drilled into the brick, concrete, or stone, as the case may be. Bolts of this type are made in quite a variety of designs. The nominal size represents the diameter of the bolt proper and not the diameter of the casing or expansion member. 当不能使用贯穿螺栓将管道吊架、支架或其他部件连接到砖块或混凝土的墙壁或天花板时，通常使用所谓的膨胀螺栓。膨胀螺栓的主体是分开的，其布置方式是，当螺栓头转动时，形成螺栓主体的部分被强制向外并靠在已钻入砖、混凝土或石头中的孔壁上，视情况而定。这种类型的螺栓有多种设计。标称尺寸代表螺栓本身的直径，而不是套管或膨胀构件的直径。 |
| Extensometer | 引伸计 |
An instrument for measuring changes in length over a given gage length caused by application or removal of a force. Commonly used in tension testing of metal specimens. Any instrument which measures the change in length of a part as the part is loaded. 一种用于测量在给定标距上由施加或移除力引起的长度变化，在零件加载时测量零件长度变化的仪器。常用于金属试样的拉力试验。 |
| External load | 外部负载 |
Forces exerted on fastener and=or joint members by such external factors as weight, wind, inertia, vibration, temperature expansion, pressure, etc. Does not equal the Working load in the fastener. 由重量、风、惯性、振动、温度膨胀、压力等外部因素施加在紧固件和/或接头构件上的力。不等于紧固件中的工作负载。 |
| Extra hard | 额外硬化 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about one-third of the way from full hard to extra spring temper. 有色合金和一些铁合金的回火，其特征是抗拉强度和硬度大约是从完全硬回火到额外弹簧回火的三分之一。 |
| Extra spring | 额外弹簧 |
A temper of nonferrous alloys and some ferrous alloys corresponding approximately to a coldworked state above full hard beyond which further cold work will not measurably increase the strength and hardness. 有色金属合金和一些铁合金的回火状态，大约对应于高于全硬的冷加工状态，超过该状态进一步冷加工将不会显着增加强度和硬度。 |
| Eyebolt (eyescrew) | 吊环螺栓（眼螺丝） |
A bolt threaded at one end and bent to a loop at the other end. A bolt or screw with a closed loop in place of a head. 一端有螺纹，另一端弯曲成环的螺栓。带有闭合环代替头部的螺栓或螺钉。 |