F436 Type 1 - ASTM F436/436M-2019

牌号	F436 Type 1
对应标准	ASTM F436/436M-2019 淬火钢垫圈的标准规范 Hardened steel washers inch and metric dimensions
归类	碳钢

F436 Type 1 化学元素成分含量(%)

	成分	P	S
Heat analysis	最小值	-	-
Heat analysis	最大值	0.04	0.05

	成分	P	S
Product analysis	最小值	-	-
Product analysis	最大值	0.05	0.06

碳当量计算

F436 Type 1 机械性能

	硬度 HBW
Through hardened washers	HRC 38~45
zinc-coated by the hot-dip	HRC 26~45

① Through hardened washers shall have a hardness of 38 to 45 HRC, except when zinc-coated by the hot-dip process, in which case they shall have a hardness of 26 to 45 HRC.
② Carburized washers shall be carburized to a minimum depth of 0.015 in. (inch series) or 0.38 mm (metric series) and shall have a surface hardness of 69 to 73 HRA or 79 to 83 HR15N, except when zinc-coated by the hot-dip process, in which case they shall have a hardness of 63 to 73 HRA or 73 to 83 HR15N.
③ Carburized and hardened washers shall have a minimum core hardness of 30 HRC or 65 HRA.

F436Type1 对应不同标准

1	ASTM F436/436M-2016 淬火钢垫圈的标准规范
	F436 Type 1
2	ASTM F436/436M-2019 淬火钢垫圈的标准规范
	F436 Type 1

注：数据仅供参考！如有疑问，请填写"我要纠错"！